The alkali-resistant coating technology of glass rod has three points

The Fiber Glass is made of medium-alkali and alkali-free Glass Fiber Fiber Glass as the base material, and is post-processed with acrylic copolymer glue. The Fiber Glass has high strength, excellent alkali resistance, acid resistance, strong adhesion to resin, and is easy to dissolve It is based on styrene and has excellent stiffness and positioning properties. It is mainly used as reinforcing materials for cement, plastics, asphalt, roofs and walls. Mainly used for GRC pre-laying, painting or mechanized forming, especially suitable for on-site construction of exterior wall insulation projects. Production technology and advantages of glass rod.

1. 14.5% to 16.7% zirconium dioxide and 6% titanium dioxide are introduced into the glass composition. After melting at a high temperature of 1600°C, platinum is leak-drawn into continuous filaments, which are spliced and twisted into textile glass fibers, and then drawn. During the process, the monofilament is coated with polymer water-soluble epoxy resin and coupling agent to ensure the affinity of the Fiber Glass with the alkali-resistant polymer during post-processing.
2. In order to further improve the safe, stable and durable performance of the glass rod, after the warp knitting is processed into leno shape, it is coated with styrene-butadiene rubber and pure acrylic emulsion again, and constant temperature, constant speed and constant tension control technology is used to make the adhesive fully effective in the early stage. Resist the erosion of the glass rod during the hydration period of polymer mortar Ca(OH)2. After coating, the anti-slip strength of the Fiber Glass intersection point is 3.5~4.5N.
3. In addition to the alkali-resistant coating, the main alkali-resistant way of the glass rod is to form a mixed film of zirconium and titanium ions on the surface of the fiber itself to prevent the erosion of alkaline substances. As time goes by, the chemical state of zirconium gradually becomes stable. The alkali resistance retention rate of glass rod is greater than 85%, which is much higher than other glass rod, so we can also call it natural glass rod.
The disadvantage of glass rod is its high production cost, which is related to zircon, rutile and melting temperature. It also has short material properties and its initial strength is not as good as that of medium-alkali and alkali-free glass rod.